Sachiya Steel International is one of the well-known manufacturers for high quality Stainless Steel 310 Wire Mesh, which contain 16 percent to 26 percent chromium and up to 35 percent nickel, which, like manganese, is a strong austenite. SS 310 Hexagonal Wire Mesh has characteristics from an invisible, self – healing chromium oxide film that forms when chromium is added at concentrations greater than 10.5 percent. The best corrosion resistance is obtained in this austenitic Stainless Steel 310S Welding Wire Mesh, where their microstructures consist of very clean crystals in which all alloying elements are held in solid solution.
Austenitic SS 310 Netting Wire Mesh cannot be hardened by heat treatment; they are also nonmagnetic. The ferritic and martensitic Stainless Steel 310S Woven Wire Mesh both have an excellent microstructure, where the latter has a higher carbon level and can be hardened and is used for knives and tools. Stainless Steel 310 Spring Steel Wire Mesh contain only up to 0.12 percent carbon, which also have chromium as their main alloy addition and practically no nickel. Corrosion resistance of this Stainless Steel 310S Fencing Wire Mesh is modest, and they are ferromagnetic. SS 310 Wire Mesh is employed at high temperatures — e.g., 800 Degree C (1,450 Degree F). Solution hardening of this Stainless Steel 310S Wire Mesh is used in this group to keep the steels strong at such heat.
|
SS 310/310S Wire mesh Specifications
|
||
| Specifications | : | ASTM A 164 ASME SA 164 |
| Standard | : | ASTM, ASME International Standards |
| Length | : | 30m to 100″ |
| Width | : | 1m to 48″ |
| Type | : | Wire Mesh , Hexagonal Wire mesh, Welding Wire mesh, Netting Wire mesh, Woven Wire mesh , Spring Steel wire mesh, Fencing Wire mesh etc. |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 – 26.00 | 0.10 max | 19.00 – 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 – 26.00 | 0.75 max | 19.00 – 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 40 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 310S | 1.4845 | S31008 | SUS 310S | 310S16 | 20Ch23N18 | – | X8CrNi25-21 |
Sachiya Steel International is one of the prominent Manufacture of high quality Stainless Steel 310H Wire Mesh, which Good resistance to mildly corrosive atmospheres, but significantly less than Grade 310H due to the Sulphur addition; the sulphide inclusions act as pit initiation sites.
Grade 310 should not be exposed to marine or other similar environments, as these will result in rapid pitting corrosion.
Because the sulphide inclusions in 310 are primarily aligned along the rolling direction the corrosion resistance is particularly reduced in cross-sections.It is like other common austenitic stainless steels, is subject to stress corrosion cracking in chloride containing environments above about 50°C.
Good oxidation resistance in intermittent service to 760°C and in continuous service to 870°C.
Welds must be annealed for maximum corrosion resistance, but even then poor mechanical and corrosion properties will result.For ultra-high machining rates there are also available special grade variants such as Ugima 303UX.
This includes copper to reduce the work hardening rate, in addition to the usual high Sulphur and Improved Machinability steel making practices.